Wire drawing die is widely used, such as high-precision wire used in electronic devices, radar, television, instrumentation and aerospace, as well as commonly used tungsten wire, molybdenum wire, stainless steel wire, wire and cable wire and various alloy wires are all diamond wire drawing dies The drawn diamond wire drawing die has strong wear resistance and extremely high service life due to the use of natural diamond as raw material.

The main failure forms of wire drawing die:
The failure of wire drawing die can be roughly divided into two categories according to the time of occurrence: normal failure and early failure.
Normal failure: After a large number of production and use, the wire drawing die wears naturally due to friction or slowly produces plastic deformation and fatigue cracks. After reaching the normal service life, the failure is a normal phenomenon, which is a normal failure.
Early failure: The mold has not reached the specified period of design and use, and early damage such as chipping, chipping, and breaking occurs; or it cannot continue to serve due to severe local wear and plastic deformation, which is an early failure. The wire drawing die manufacturer tells you that for the early failure of the mold, you must find the cause and try to take remedial measures.